Alkyl phenolic resin and method of preparation thereof

ABSTRACT

Described herein are alkyl phenolic resins and methods of producing them. The content of residual phenol in the alkyl phenolic resin may be less than about 2% w/w, the softening point of the alkyl phenolic resin may be about 85° C. to about 105° C., the tackiness of the alkyl phenolic resin may be about 8 N to about 25 N, the alkyl group of the alkyl phenol may have 6-12 carbon atoms, and the content of 4-(1,1,3,3-tetramethylbutyl) phenol in the alkyl phenol may be from about 0% to about 85% w/w. The invention also relates to a use of the alkyl phenolic resin as rubber tackifier.

RELATED APPLICATIONS

This application is a Continuation of Ser. No. 14/064,708 filed Oct. 28,2013 which claims the benefit and is a continuation in part of PCTInternational Application number PCT/CN2012/081500, filed Sep. 17, 2012,the contents of which are hereby incorporated by reference.

TECHNICAL FIELD

In certain embodiments, the invention relates to an alkyl phenolic resinwith low quantities of residual phenol. In certain embodiments, theinvention relates to methods of preparing the inventive alkyl phenolicresin. In certain embodiments, the invention relates to the use of thealkyl phenolic resin as rubber tackifier. In certain embodiments, theinvention relates to rubber compounds comprising the alkyl phenolicresin.

BACKGROUND OF THE INVENTION

Alkyl phenols are important intermediates in the synthesis of rawmaterials for the production of fine chemicals. Alkyl phenols may besynthesized by reacting an alkene and a phenol in the presence of acidiccatalyst. Alkyl phenols have broad applications in the production ofnon-ionic surfactants, anti-oxidants, oil additives, phenolic resin, andso on. An important alkyl phenol is p-tert-octyl phenol [PTOP, or4-(1,1,3,3-tetramethylbutyl) phenol] because of its use in theproduction of phenolic resins; p-tert-octyl phenolic resin is widelyused as rubber tackifier to produce rubber products, such as tires.

As described in CN101161616A, PTOP may be synthesized as follows: (a)Di-isobutylene (DIB) is obtained by the selective polymerization ofisobutylene. The main components of di-isobutylene synthesized in thisway are 2,4,4-trimethyl-1-pentene and 2,4,4-trimethyl-2-pentene. (b) DIBand phenol are reacted under acidic conditions to obtain an alkyl phenolwith a highly branched alkyl chain.

However, isobutylene has broad applications in, for example, theproduction of butyl rubber, oil additives, methyl tert-butyl ether(MTBE), isobutyl alcohol, and other chemicals. Therefore, the supply ofisobutylene for DIB production is scarce.

In the rubber industry, p-tert-octyl phenolic resin is often used as atackifying resin, which usually contains certain amount (2-6% w/w) ofresidual, free PTOP due to synthetic limitations. Because PTOP is apollutant, reducing the content of free PTOP in the resin is animportant industrial goal. Practical experience proves that increasingthe aldehyde-phenol ratio during resin production may reduce the contentof free PTOP. However, the application of alkyl phenolic resin in therubber industry dictates that the softening point of the resin bebetween 85° C. and 105° C., which facilitates the mixing and dispersionof the alkyl phenolic resin in rubber matrix, improving the rubbertackiness. Traditionally, the aldehyde-phenol molar ratio duringsynthesis of p-tert-octyl phenolic resin is between 0.7 and 0.9. Infact, when this ratio is above 0.8, the resin's softening point is oftenabove 105° C. Hence, by known methods, it is impossible to reduce theresidual PTOP content in the resin by increasing the aldehyde-phenolratio. In addition, the decrease of free phenol content also improvesthe tackifying effect of the resin.

U.S. Pat. No. 7,772,345B2 describes a means of reducing free alkylphenol content in alkyl phenolic resin by reacting vinyl compounds andfree alkyl phenol. However the dosage of vinyl compounds is relativelylarge, and oligomers that do not contribute to the tackifying propertywill be produced at high temperatures.

CN 1863832A mentions the use of fatty acids to plasticize tackifyingresin, thereby increasing the aldehyde-phenol ratio during reaction inorder to reduce free phenol. But fatty acids are detrimental to rubbertackiness, and fatty acids will react with zinc oxide in the rubberformulation step, influencing the vulcanization process.

Therefore, it is desirable to offer an alkyl phenolic resin that hasless than 2% (w/w) of residual phenol and properties (such as tackinessand softening point) suitable for use in rubber compositions.

SUMMARY OF THE INVENTION

In certain embodiments, the invention relates to a method, comprising:

contacting a first phenol and a second phenol with an aldehyde at afirst temperature for a first amount of time, thereby forming an alkylphenolic resin,

wherein

the first phenol is an alkyl phenol;

the second phenol is different from the first phenol; and

the second phenol is present in a concentration from about 0% to about10% by weight of total phenol.

In certain embodiments, the invention relates to an alkyl phenolic resinmade by any one of the aforementioned methods.

In certain embodiments, the invention relates to a composition, whereinthe composition consists essentially of a polycondensation product of(i) a first phenol and a second phenol with (ii) an aldehyde;

the first phenol is an alkyl phenol;

the second phenol is different from the first phenol; and

the second phenol is present in a concentration from about 0% to about10% by weight of total phenol.

In certain embodiments, the invention relates to the use of any one ofthe aforementioned compositions, or an alkyl phenolic resin made by anyone of the aforementioned methods, as an adhesive, a dispersant, anelastomer, a coating, a paint, a thermoplastic elastomer, an inkcomponent, a lubricant, or a rubber tackifier.

In certain embodiments, the invention relates to the use of any one ofthe aforementioned compositions, or an alkyl phenolic resin made by anyone of the aforementioned methods, in an adhesive, a dispersant, anelastomer, a coating, a paint, a thermoplastic elastomer, an inkcomponent, a lubricant, a rubber, or a rubber tackifier.

In certain embodiments, the invention relates to the use of any one ofthe aforementioned compositions, or an alkyl phenolic resin made by anyone of the aforementioned methods, in the manufacture of an adhesive, adispersant, an elastomer, a coating, a paint, a thermoplastic elastomer,an ink component, a lubricant, a rubber, or a rubber tackifier.

In certain embodiments, the invention relates to a rubber article,wherein the rubber article comprises (i) a rubber component, and (ii)any one of the aforementioned compositions or an alkyl phenolic resinmade by any one of the aforementioned methods.

DETAILED DESCRIPTION Overview

In certain embodiments, the invention relates to the surprisingdiscovery that, during preparation of alkyl phenolic resins, by reducingthe proportion of highly-branched 4-(1,1,3,3-tetramethylbutyl) phenol inthe alkyl phenols, it is possible to reduce residual phenol whilemaintaining the application properties of the produced phenolic resin.

In certain embodiments, the invention relates to an alkyl phenolic resinwith low content of residual phenol, good tackiness, and/or suitablesoftening point. In certain embodiments the alkyl phenolic resin of theinvention has one or more of the following characteristics: no more than2% w/w residual phenol, a softening point from about 85° C. to about105° C., or a tackiness from about 8 N to about 25 N. In certainembodiments, the alkyl group of the alkyl phenol has 6-12 carbon atoms.In certain embodiments, the content of 4-(1,1,3,3-tetramethylbutyl)phenol in the alkyl phenol is from about 0% to about 85% w/w.

In certain embodiments, the invention relates to a method of preparingthe alkyl phenolic resin. In certain embodiments, the method involvesreacting an alkyl phenol and an arbitrarily selected phenol (0-10% w/wof total phenol) and aldehyde.

In certain embodiments, the invention relates to rubber compounds thatcontain the alkyl phenolic resin.

Definitions

As used herein, the terms “a,” “an,” “the,” “one or more,” and “at leastone” are used interchangeably and include plural referents unless thecontext clearly dictates otherwise.

Unless defined otherwise, all scientific and technical terms areunderstood to have the same meaning as commonly used in the art to whichthey pertain. For the purpose of the present disclosure, additionalspecific terms are defined throughout.

The terms “comprises,” “includes” and variations of these words do nothave a limiting meaning where these terms appear in the description andclaims. Thus, for example, a process that comprises “an” alkyl phenolcan be interpreted to mean a process that includes “one or more” alkylphenols. In addition, the term “comprising,” which is synonymous with“including” or “containing,” is inclusive, open-ended, and does notexclude additional un-recited elements or process steps.

As used herein, the term “and/or” means one, more than one, or all ofthe listed elements.

Also herein, the recitations of numerical ranges by endpoints includeall numbers subsumed within that range (e.g., 1 to 5 includes 1, 1.5, 2,2.75, 3, 3.80, 4, 5, etc.).

As used herein, the term “concentration” refers to a measure of anamount of a substance.

As used herein, the term “alkyl” means a saturated linear (i.e.,straight chain), cyclic (i.e., cycloaliphatic), or branched monovalenthydrocarbon group including, e.g. methyl, ethyl, n-propyl, isopropyl,t-butyl, amyl, heptyl, dodecyl, octadecyl, 2-ethylhexyl, and the like.

As used herein, the term “alkylene” or “alkene” means an unsaturated,linear or branched monovalent hydrocarbon group with one or moreolefinically unsaturated groups (i.e., carbon-carbon double bonds), suchas a vinyl group.

Exemplary Methods

In certain embodiments, the invention relates to a method, comprising:

contacting a first phenol and a second phenol with an aldehyde at afirst temperature for a first amount of time, thereby forming an alkylphenolic resin,

wherein

the first phenol is an alkyl phenol;

the second phenol is different from the first phenol; and

the second phenol is present in a concentration from about 0% to about10% by weight of total phenol.

In certain embodiments, the invention relates to any one of theaforementioned methods, wherein the total phenol is the sum of theweights of the first phenol and the second phenol.

In certain embodiments, the invention relates to any one of theaforementioned methods, wherein the first phenol and the second phenolare contacted with the aldehyde in the presence of acidic catalyst. Incertain embodiments, the invention relates to any one of theaforementioned methods, wherein the acidic catalyst is selected from thegroup consisting of sulfuric acid, hydrochloric acid, phosphoric acid,toluenesulfonic acid, xylenesulfonic acid, benzenesulfonic acid, benzenedisulfonic acid, phenol sulfonic acid, C1-C15 alkyl benzene sulfonicacid (such as p-methylbenzene sulfonic acid), naphthalene sulfonic acid,and oxalic acid, or their mixture.

In certain embodiments, the invention relates to any one of theaforementioned methods, wherein the molar ratio of aldehyde-to-phenol isfrom about 0.8:1 to about 1.2:1. In certain embodiments, the inventionrelates to any one of the aforementioned methods, wherein the molarratio of aldehyde-to-phenol is from about 0.8:1 to about 1:1. In certainembodiments, the invention relates to any one of the aforementionedmethods, wherein the molar ratio of aldehyde-to-phenol is about 0.8:1,about 0.9:1, or about 1:1.

In certain embodiments, the invention relates to any one of theaforementioned methods, wherein the first temperature and the firstamount of time are conditions sufficient to form an alkyl phenolicresin.

In certain embodiments, the invention relates to any one of theaforementioned methods, wherein the first phenol, the second phenol, andthe aldehyde are contacted in the presence of a first solvent. Incertain embodiments, the first solvent comprises water. In certainembodiments, the first solvent is water.

In certain embodiments, the invention relates to any one of theaforementioned methods, wherein the first temperature is the refluxtemperature of the first phenol, the second phenol, and the aldehyde. Incertain embodiments, the invention relates to any one of theaforementioned methods, wherein the first temperature is the refluxtemperature of the first phenol, the second phenol, and the aldehyde ina first solvent. In certain embodiments, the first solvent compriseswater.

In certain embodiments, the invention relates to any one of theaforementioned methods, wherein the first period of time is from about 1h to about 3 h. In certain embodiments, the invention relates to any oneof the aforementioned methods, wherein the first period of time is about1 h, about 1.5 h, about 2 h, about 2.5 h, or about 3 h.

In certain embodiments, the invention relates to any one of theaforementioned methods, wherein the first temperature is from about 80°C. to about 120° C. In certain embodiments, the invention relates to anyone of the aforementioned methods, wherein the first temperature isabout 80° C., about 85° C., about 90° C., about 95° C., about 100° C.,about 105° C., about 110° C., about 115° C., or about 120° C.

In certain embodiments, the invention relates to any one of theaforementioned methods, wherein the reaction of the first phenol, thesecond phenol, and the aldehyde results in a first reaction mixture. Incertain embodiments, the invention relates to any one of theaforementioned methods, further comprising the step of distilling thefirst reaction mixture, thereby forming a second reaction mixture. Incertain embodiments, the first reaction mixture is distilled for aperiod of time from about 0.5 h to about 2 h. In certain embodiments,the first reaction mixture is distilled for a period of time of about0.5 h, about 1 h, about 1.5 h, or about 2 h. In certain embodiments, thefirst reaction mixture is distilled at a temperature of from about 130°C. to about 200° C. In certain embodiments, the first reaction mixtureis distilled at a temperature of about 130° C., about 140° C., about150° C., about 160° C., about 170° C., about 180° C., about 190° C., orabout 200° C.

In certain embodiments, the invention relates to any one of theaforementioned methods, further comprising the step of adding aneutralizer to the second reaction mixture, thereby forming a thirdreaction mixture.

In certain embodiments, the invention relates to any one of theaforementioned methods, wherein the neutralizer is selected from thegroup consisting of: a hydroxide or a carbonate of an alkali metal or analkaline earth metal, aqueous ammonia, and an amine. In certainembodiments, the invention relates to any one of the aforementionedmethods, wherein the neutralizer is selected from the group consistingof sodium hydroxide, potassium hydroxide, calcium hydroxide, potassiumcarbonate, and sodium carbonate. In certain embodiments, the inventionrelates to any one of the aforementioned methods, wherein theneutralizer is selected from the group consisting of a C1-C6 alkylamine, triethanolamine, diethanolamine, triethylamine,1,8-diazabicyclo(5, 4, 0)undec-7-ene (DBU), triethylenetetramine,diethylenetriamine, and tetraethylenepentamine, or their mixture.

In certain embodiments, the invention relates to any one of theaforementioned methods, further comprising the step of distilling thethird reaction mixture. In certain embodiments, the third reactionmixture is distilled under negative pressure. In certain embodiments,the third reaction mixture is distilled at a negative pressure of fromabout 2 kPa to about 3 kPa.

In certain embodiments, the invention relates to any one of theaforementioned methods, wherein the aldehyde is selected from RCHO; andR is hydrogen or C1-C8 alkyl. In certain embodiments, the inventionrelates to any one of the aforementioned methods, wherein the aldehydeis selected from the group consisting of formaldehyde, acetaldehyde,n-butylaldehyde, n-pentaldehyde, n-hexylaldehyde, and heptyl aldehyde,formaldehyde trimer, acetaldehyde trimer, furaldehyde, benzaldehyde, andβ-hydroxybutylaldehyde.

In certain embodiments, the invention relates to any one of theaforementioned methods, wherein the second phenol is selected from thegroup consisting of phenol, m-dihydroxybenzene, and xylenol.

In certain embodiments, the invention relates to any one of theaforementioned methods, wherein the alkyl phenol is commerciallyacquired.

In certain embodiments, the invention relates to any one of theaforementioned methods, further comprising the step of preparing thealkyl phenol.

In certain embodiments, the invention relates to any one of theaforementioned methods, wherein the alkyl phenol is prepared byalkylation of phenol using a monoalkene.

In certain embodiments, the invention relates to any one of theaforementioned methods, wherein the alkylation of phenol is carried outat a second temperature for a second period of time. In certainembodiments, the second temperature is from about 80° C. to about 100°C. In certain embodiments, the second temperature is about 80° C., about85° C., about 90° C., about 95° C., or about 100° C. In certainembodiments, the second period of time is from about 2.5 h to about 10h. In certain embodiments, the second period of time is about 2.5 h,about 3 h, about 3.5 h, about 4 h, about 4.5 h, about 5 h, about 5.5 h,about 6 h, about 6.5 h, about 7 h, about 7.5 h, about 8 h, about 8.5 h,about 9 h, about 9.5 h, or about 10 h. In certain embodiments, theinvention relates to any one of the aforementioned methods, wherein themolar ratio of monoalkene-to-phenol is from about 2:1 to about 1:1. Incertain embodiments, the molar ratio of monoalkene-to-phenol is about2:1, about 1.9:1, about 1.8:1, about 1.7:1, about 1.6:1, about 1.5:1,about 1.4:1, about 1.3:1, about 1.2:1, about 1.1:1, or about 1:1.

In certain embodiments, the invention relates to any one of theaforementioned methods, wherein the reaction between phenol and themonoalkene is carried out in the presence of an alkylation catalyst. Incertain embodiments, the invention relates to any one of theaforementioned methods, wherein the reaction between phenol and themonoalkene is carried out in the presence of an alkylation catalyst; andthe alkylation catalyst is an ion exchange resin or an activatedclay-phosphoric acid. In certain embodiments, the invention relates toany one of the aforementioned methods, wherein the ion exchange resin isan acidic ion exchange resin. In certain embodiments, the inventionrelates to any one of the aforementioned methods, wherein the ionexchange resin is a strongly acidic ion exchange resin.

In certain embodiments, the invention relates to any one of theaforementioned methods, wherein the reaction between phenol and themonoalkene is carried out in the presence of an alkylation catalyst; andfrom about 2 parts to about 10 parts (w/w) of alkylation catalyst areused for every 100 parts phenol. In certain embodiments, the inventionrelates to any one of the aforementioned methods, wherein the reactionbetween phenol and the monoalkene is carried out in the presence of analkylation catalyst; and about 2 parts, about 3 parts, about 4 parts,about 5 parts, about 6 parts, about 7 parts, about 8 parts, about 9parts, or about 10 parts (w/w) of alkylation catalyst are used for every100 parts phenol.

In certain embodiments, the invention relates to any one of theaforementioned methods, wherein the monoalkene is a monoalkene mixture.In certain embodiments, the invention relates to any one of theaforementioned methods, wherein the monoalkene comprises, consistsessentially of, or consists of C6-C12 monoalkenes. In certainembodiments, the invention relates to any one of the aforementionedmethods, wherein the monoalkene comprises, consists essentially of, orconsists of C8-C10 monoalkenes. In certain embodiments, the inventionrelates to any one of the aforementioned methods, wherein the content of2,4,4-trimethyl-1-pentene or 2,4,4-trimethyl-2-pentene in the monoalkeneis from about 0% to about 85% w/w. In certain embodiments, the inventionrelates to any one of the aforementioned methods, wherein the content of2,4,4-trimethyl-1-pentene or 2,4,4-trimethyl-2-pentene in the monoalkeneis from about 2% to about 60% w/w. In certain embodiments, the inventionrelates to any one of the aforementioned methods, wherein the content of2,4,4-trimethyl-l-pentene or 2,4,4-trimethyl-2-pentene in the monoalkeneis from about 2% to about 40% w/w. In certain embodiments, the inventionrelates to any one of the aforementioned methods, wherein the content of2,4,4-trimethyl-1-pentene or 2,4,4-trimethyl-2-pentene in the monoalkeneis from about 5% to about 20% w/w. In certain embodiments, the inventionrelates to any one of the aforementioned methods, wherein the content of2,4,4-trimethyl-l-pentene or 2,4,4-trimethyl-2-pentene in the monoalkeneis about 4%, about 5%, about 6%, about 7%, about 8%, about 9%, about10%, about 11%, about 12%, about 13%, about 14%, about 15%, about 16%,about 17%, about 18%, about 19%, or about 20% w/w. In certainembodiments, the monoalkene mixture contains only one monoalkene.

In certain embodiments, the invention relates to any one of theaforementioned methods, wherein the reaction between phenol and themonoalkene is carried out until from about 85% to about 100% w/w of thephenol is converted into alkyl phenol. In certain embodiments, theinvention relates to any one of the aforementioned methods, wherein thereaction between phenol and the monoalkene is carried out until fromabout 90% to about 100% w/w of the phenol is converted into alkylphenol. In certain embodiments, the invention relates to any one of theaforementioned methods, wherein the product of the reaction betweenphenol and the monoalkene is used to react with aldehyde to form alkylphenolic resin. In certain embodiments, the invention relates to any oneof the aforementioned methods, wherein the product of the reactionbetween phenol and the monoalkene is used, without purification, toreact with aldehyde to form the alkyl phenolic resin.

In certain embodiments, the invention relates to any one of theaforementioned methods, further comprising the step of synthesizing themonoalkene. In certain embodiments, the invention relates to any one ofthe aforementioned methods, wherein the monoalkene is synthesized bynon-selective polymerization. During non-selective polymerization, forexample non-selective polymerization of C4 alkenes, highly-activecatalyst is used at higher temperatures so that all butylenes react toobtain various octylene isomers. U.S. Pat. No. 4,334,118A describes theoligomerization (i.e., non-selective polymerization) of C3 -C12 alkenes.CN1058729A describes the catalyst and process parameters that can beapplied to alkene polymerization. These openly-available publicationsare all cited herein as reference and hereby incorporated by referencein their entirety.

Main octylene components obtained through non-selective polymerizationinclude 2,2-dimethyl-3-hexene, 2,4,4-trimethyl-1-pentene,2,4,4-trimethyl-2-pentene, 3-isopropyl-1-pentene, 4,4-dimethyl-2-hexene,2-isopropyl-1-pentene, 3,4,4-trimethyl-2-pentene, 2,3-dimethyl-3-hexene,3-isopropyl-2-pentene, cis-2,3-dimethyl-2-hexene, 2-ethyl-3-hexene,2,3,4-trimethyl-2-pentene, 2-ethyl-1-hexene, 3-methyl-3-heptylene,cis-2,3-dimethyl-3-hexene, 3-ethyl-2-hexene, andtrans-2,3-dimethyl-3-hexene.

In certain embodiments, the invention relates to any one of theaforementioned methods, wherein the monoalkene comprises a C8 alkene;and the concentration of DIB (2,4,4-trimethyl-1-pentene and2,4,4-trimethyl-2-pentene) in the C8 alkenes is from about 0% to about1.5% w/w. In certain embodiments, the invention relates to any one ofthe aforementioned methods, wherein the monoalkene comprises a C8alkene; and the concentration of DIB (2,4,4-trimethyl-1-pentene and2,4,4-trimethyl-2-pentene) in the C8 alkenes is about 0%, about 0.5%,about 1%, or about 1.5% w/w.

In certain embodiments, the invention relates to any one of theaforementioned methods, wherein the monoalkene comprises octyleneobtained through non-selective polymerization; and the octylenecomprises multiple components with a lower degree of branching than DIB.

In certain embodiments, the invention relates to any one of theaforementioned methods, wherein the monoalkenes in the monoalkenemixture are selected from the group consisting of:2,4,4-trimethyl-1-pentene, 2,4,4-trimethyl-2-pentene, octylene,nonylene, and dodecene. In certain embodiments, the invention relates toany one of the aforementioned methods, wherein the octylene was obtainedthrough non-selective polymerization of C4 alkenes. In certainembodiments, the invention relates to any one of the aforementionedmethods, wherein the nonylene was obtained through non-selectivepolymerization of C3 alkenes. In certain embodiments, the inventionrelates to any one of the aforementioned methods, wherein the dodecenewas obtained through non-selective polymerization of C6 alkenes.

In certain embodiments, the invention relates to any one of theaforementioned methods, wherein the monoalkene other than2,4,4-trimethyl-1-pentene and 2,4,4-trimethyl-2-pentene in themonoalkene mixture is octylene obtained through non-selectivepolymerization of a C4 alkene, in which the C4 alkene comprisesisobutylene, 1-butylene, or 2-butylene.

In certain embodiments, the invention relates to any one of theaforementioned methods, wherein the non-selective polymerization iscarried out in the presence of strong acid. In certain embodiments, theinvention relates to any one of the aforementioned methods, wherein thenon-selective polymerization is carried out in the presence ofphosphoric acid. In certain embodiments, the invention relates to anyone of the aforementioned methods, wherein the non-selectivepolymerization is carried out in the presence of solid phosphoric acid.In certain embodiments, the invention relates to any one of theaforementioned methods, wherein the non-selective polymerization iscarried out in the presence of phosphoric acid loaded onto silicondioxide.

In certain embodiments, the invention relates to any one of theaforementioned methods, wherein the non-selective polymerization iscarried out at a third temperature. In certain embodiments, the thirdtemperature is from about 160° C. to about 220° C. In certainembodiments, the third temperature is about 160° C., about 170° C.,about 180° C., about 190° C., about 200° C., about 210° C., or about220° C.

In certain embodiments, the invention relates to any one of theaforementioned methods, wherein the alkyl group of the alkyl phenol hasfrom about 6 to about 12 carbon atoms. In certain embodiments, theinvention relates to any one of the aforementioned methods, wherein thealkyl group of the alkyl phenol has about 6, about 7, about 8, about 9,about 10, about 11, or about 12 carbon atoms.

In certain embodiments, the invention relates to any one of theaforementioned methods, wherein the concentration of4-(1,1,3,3-tetramethylbutyl) phenol in the alkyl phenol is from about 0%to about 85% w/w. In certain embodiments, the invention relates to anyone of the aforementioned methods, wherein the concentration of4-(1,1,3,3-tetramethylbutyl) phenol in the alkyl phenol is about 0%,about 5%, about 10%, about 15%, about 20%, about 25%, about 30%, about35%, about 40%, about 45%, about 50%, about 55%, about 60%, about 65%,about 70%, about 75%, about 80%, or about 85% w/w.

In certain embodiments, the invention relates to an alkyl phenolic resinmade by any one of the aforementioned methods.

Exemplary Compositions

In certain embodiments, the invention relates to a composition, whereinthe composition consists essentially of a polycondensation product of(i) a first phenol and a second phenol with (ii) an aldehyde; the firstphenol is an alkyl phenol; the second phenol is different from the firstphenol; and the second phenol is present in a concentration from about0% to about 10% by weight of total phenol.

In certain embodiments, the invention relates to any one of theaforementioned compositions, wherein the composition is an alkylphenolic resin.

In certain embodiments, the invention relates to any one of theaforementioned compositions, wherein the aldehyde is selected from RCHO,wherein R is hydrogen or C1-C8 alkyl. In certain embodiments, theinvention relates to any one of the aforementioned compositions, whereinthe aldehyde is selected from the group consisting of formaldehyde,acetaldehyde, n-butylaldehyde, n-pentaldehyde, n-hexylaldehyde, heptylaldehyde, formaldehyde trimer, acetaldehyde trimer, furaldehyde,benzaldehyde, and β-hydroxybutylaldehyde.

In certain embodiments, the invention relates to any one of theaforementioned compositions, wherein the composition comprises residualphenol in an amount of from about 0% to about 2% by weight. In certainembodiments, the invention relates to any one of the aforementionedcompositions, wherein the composition comprises residual phenol in anamount of from about 0% to about 0.8% by weight. In certain embodiments,the invention relates to any one of the aforementioned compositions,wherein the composition comprises residual phenol in an amount of about0%, about 0.1%, about 0.2%, about 0.3%, about 0.4%, about 0.5%, about0.6%, about 0.7%, about 0.8%, about 0.9%, about 1%, about 1.5%, or about2% by weight.

In certain embodiments, the invention relates to any one of theaforementioned compositions, wherein the composition has a softeningpoint of about 85° C. to about 105° C. In certain embodiments, theinvention relates to any one of the aforementioned compositions, whereinthe composition has a softening point of about 95° C. to about 105° C.In certain embodiments, the invention relates to any one of theaforementioned compositions, wherein the composition has a softeningpoint of about 95° C., about 100° C., or about 105° C. In certainembodiments, the invention relates to any one of the aforementionedcompositions, wherein the softening point is measured according to ASTMD3461-97(2007)).

In certain embodiments, the invention relates to any one of theaforementioned compositions, wherein the composition has a tackinessfrom about 8 N to about 25 N. In certain embodiments, the inventionrelates to any one of the aforementioned compositions, wherein thecomposition has a tackiness from about 9 N to about 20 N. In certainembodiments, the invention relates to any one of the aforementionedcompositions, wherein the composition has a tackiness of about 9 N,about 10 N, about 11 N, about 12 N, about 13 N, about 14 N, about 15 N,about 16 N, about 17 N, about 18 N, about 19 N, or about 20 N. Incertain embodiments, the invention relates to any one of theaforementioned compositions, wherein the tackiness is measured accordingto JIS T 9233-1997.

In certain embodiments, the invention relates to any one of theaforementioned compositions, wherein the alkyl group of the alkyl phenolhas 6-12 carbon atoms. In certain embodiments, the invention relates toany one of the aforementioned compositions, wherein the alkyl group ofthe alkyl phenol has 8-10 carbon atoms. In certain embodiments, theinvention relates to any one of the aforementioned compositions, whereinthe alkyl phenol is hexyl phenol, heptyl phenol, octyl phenol, nonylphenol, decyl phenol, undecyl phenol, dodecyl phenol or their isomersand mixtures. In certain embodiments, the invention relates to any oneof the aforementioned compositions, wherein the alkyl phenol is octylphenol, nonyl phenol, decyl phenol, or their isomers and mixtures.

In certain embodiments, the invention relates to any one of theaforementioned compositions, wherein the content of4-(1,1,3,3-tetramethylbutyl) phenol in the alkyl phenol is from about 0%to about 85% w/w. In certain embodiments, the invention relates to anyone of the aforementioned compositions, wherein the content of4-(1,1,3,3-tetramethylbutyl) phenol in the alkyl phenol is from about 2%to about 60% w/w. In certain embodiments, the invention relates to anyone of the aforementioned compositions, wherein the content of4-(1,1,3,3-tetramethylbutyl) phenol in the alkyl phenol is from about 2%to about 40% w/w. In certain embodiments, the invention relates to anyone of the aforementioned compositions, wherein the content of4-(1,1,3,3-tetramethylbutyl) phenol in the alkyl phenol is from about 5%to about 20% w/w. In certain embodiments, the invention relates to anyone of the aforementioned compositions, wherein the content of4-(1,1,3,3-tetramethylbutyl) phenol in the alkyl phenol is about 5%,about 10%, about 15%, or about 20% w/w.

Exemplary Uses

In certain embodiments, the invention relates to the use of any one ofthe aforementioned alkyl phenolic resins, or the use of an alkylphenolic resin made by any one of the aforementioned methods, as anadhesive, a dispersant, an elastomer, a coating, a paint, athermoplastic elastomer, an ink component, a lubricant, or a rubbertackifier.

In certain embodiments, the invention relates to the use of any one ofthe aforementioned alkyl phenolic resins, or the use of an alkylphenolic resin made by any one of the aforementioned methods, in anadhesive, a dispersant, an elastomer, a coating, a paint, athermoplastic elastomer, an ink component, a lubricant, a rubber, or arubber tackifier.

In certain embodiments, the invention relates to the use of any one ofthe aforementioned alkyl phenolic resins, or the use of an alkylphenolic resin made by any one of the aforementioned methods, in themanufacture of an adhesive, a dispersant, an elastomer, a coating, apaint, a thermoplastic elastomer, an ink component, a lubricant, arubber, or a rubber tackifier.

Exemplary Articles

In certain embodiments, the invention relates to a rubber article,wherein the rubber article comprises (i) a rubber component, and (ii)any one of the aforementioned alkyl phenolic resins or an alkyl phenolicresin made by any one of the aforementioned methods.

In certain embodiments, the invention relates to any one of theaforementioned rubber articles, wherein the rubber component comprisesnatural rubber, synthetic rubber, or their mixture. In certainembodiments, synthetic rubber comprises cis-1,4-polyisoprene,polybutadiene, polychlorobutadiene, isoprene/butadiene copolymer,acrylonitrile/butadiene copolymer, acrylonitrile/isoprene copolymer,styrene/butadiene/isoprene copolymer, butyl rubber, ethylene propylenediene (M-class) (EPDM) rubber, or styrene/butadiene copolymer.

In certain embodiments, the invention relates to any one of theaforementioned rubber articles, wherein the rubber article comprises thealkyl phenolic resin at a concentration from about 0.5 parts to about 7parts/100 parts of rubber (w/w). In certain embodiments, the inventionrelates to any one of the aforementioned rubber articles, wherein therubber article comprises the alkyl phenolic resin at a concentrationfrom about 1 part to about 5 parts/100 parts of rubber (w/w). In certainembodiments, the invention relates to any one of the aforementionedrubber articles, wherein the rubber article comprises the alkyl phenolicresin at a concentration of about 1 part, about 1.5 parts, about 2parts, about 2.5 parts, about 3 parts, about 3.5 parts, about 4 parts,about 4.5 parts, or about 5 parts per 100 parts of rubber (w/w).

In certain embodiments, the invention relates to any one of theaforementioned rubber articles, wherein the rubber article comprises asecond resin. In certain embodiments, the invention relates to any oneof the aforementioned rubber articles, wherein the rubber articlecomprises a second resin; and the second resin is not an alkyl phenolicresin.

Exemplary Embodiments

In certain embodiments, the invention relates to an alkyl phenolicresin, which is produced through the reaction between alkyl phenol andother arbitrarily selected phenol (0-10% w/w of total phenol) andaldehyde, in which, the content of residual phenol in the alkyl phenolicresin is no more than 2% w/w, the softening point is 85-105° C.(measured according to ASTM D3461-97(2007)), the tackiness is 8-25 N(measured according to JIS T 9233-1997), the alkyl group of the alkylphenol has 6-12 carbon atoms, and the content of4-(1,1,3,3-tetramethylbutyl) phenol in the alkyl phenol is 0-85% w/w.

In certain embodiments, the invention relates to any one of theaforementioned alkyl phenolic resins, wherein the content of residualphenol in the alkyl phenolic resin is no more than 1.5% w/w, no morethan 1% w/w, or no more than 0.8% w/w.

In certain embodiments, the invention relates to any one of theaforementioned alkyl phenolic resins, wherein the content of4-(1,1,3,3-tetramethylbutyl) phenol in the alkyl phenol is 2-60% w/w,2-40% w/w, or 5-20% w/w.

In certain embodiments, the invention relates to any one of theaforementioned alkyl phenolic resins, wherein the alkyl group of thealkyl phenol has 8-10 carbon atoms.

In certain embodiments, the invention relates to any one of theaforementioned alkyl phenolic resins, wherein the alkyl phenol isprepared by alkylation of phenol using monoalkene, in which themonoalkene is C6-C12 monoalkene, or C8-C10 monoalkene; the content of2,4,4-trimethyl-l-pentene and 2,4,4-trimethyl-2-pentene in themonoalkene is 0-85% w/w, 2-60% w/w, 2-40% w/w, or 5-20% w/w.

In certain embodiments, the invention relates to any one of theaforementioned alkyl phenolic resins, wherein the alkenes other than2,4,4-trimethyl-1-pentene and 2,4,4-trimethyl-2-pentene in themonoalkene are selected from octylene obtained through non-selectivepolymerization of C4 alkenes, nonylene obtained through non-selectivepolymerization of C3 alkenes, and dodecene obtained throughnon-selective polymerization of C6 alkenes.

In certain embodiments, the invention relates to any one of theaforementioned alkyl phenolic resins, wherein the non-selectivepolymerization takes place under the conditions of strong acid and hightemperature of 160-220° C.

In certain embodiments, the invention relates to any one of theaforementioned alkyl phenolic resins, wherein the alkenes other than2,4,4-trimethyl-1-pentene and 2,4,4-trimethyl-2-pentene in themonoalkene is octylene obtained through non-selective polymerization ofC4 alkene(s), in which the C4 alkene(s) is one or more of isobutylene,1-butylene and 2-butylene.

In certain embodiments, the invention relates to any one of theaforementioned alkyl phenolic resins, wherein the alkylation of phenolwith monoalkene is carried out in the presence of alkylation catalyst,and the catalyst is selected from strongly acidic ionic exchange resinand activated clay-phosphoric acid.

In certain embodiments, the invention relates to any one of theaforementioned alkyl phenolic resins, wherein the alkylation reaction iscarried out until the conversion rate of phenol is above 85% w/w, orabove 90% w/w, and the reaction product is used to react with aldehydeto form alkyl phenolic resin.

In certain embodiments, the invention relates to any one of theaforementioned alkyl phenolic resins, wherein the alkylation reactionbetween monoalkene and phenol is carried out at 80-100° C. and takes2.5-10 hours; the monoalkene-phenol molar ratio is 2:1-1:1, in which2-10 parts (w/w) of alkylation catalyst are used for every 100 parts ofphenol.

In certain embodiments, the invention relates to any one of theaforementioned alkyl phenolic resins, wherein the aldehyde is selectedfrom RCHO, in which R is hydrogen or alkyl with 1-8 carbon atoms, suchas formaldehyde, acetaldehyde, n-butylaldehyde, n-pentaldehyde,n-hexylaldehyde and heptyl aldehyde, as well as formaldehyde oligomers,such as formaldehyde trimer, acetaldehyde trimer, furaldehyde,benzaldehyde and β-hydroxybutylaldehyde; the other phenol is selectedfrom phenol, m-dihydroxybenzene, and xylenol.

In certain embodiments, the invention relates to any one of theaforementioned alkyl phenolic resins, wherein the aldehyde-phenol molarratio is 0.8:1-1.2:1, or 0.8:1-1:1.

In certain embodiments, the invention relates to any one of theaforementioned alkyl phenolic resins, wherein the softening point of thealkyl phenolic resin is 95-105° C. (measured according to ASTMD3461-97(2007)).

In certain embodiments, the invention relates to any one of theaforementioned alkyl phenolic resins, wherein the tackiness of the alkylphenolic resin is 9-20 N (measured according to JIS T 9233-1997).

In certain embodiments, the invention relates to a method of preparingany one of the aforementioned alkyl phenolic resins, wherein the resinis produced through the reaction between alkyl phenol and otherarbitrarily selected phenol (0-10% w/w of total phenol) and aldehyde, inwhich the alkyl group of the alkyl phenol has 6-12 carbon atoms, and thecontent of 4-(1,1,3,3-tetramethylbutyl) phenol in the alkyl phenol is0-85% w/w.

In certain embodiments, the invention relates to any one of theaforementioned methods, wherein the reaction is carried out in thepresence of acidic catalyst, in which the acidic catalyst is one ofsulfuric acid, hydrochloric acid, phosphoric acid, toluenesulfonic acid,xylenesulfonic acid, benzenesulfonic acid, benzene disulfonic acid,phenol sulfonic acid, C1-C15 alkyl benzene sulfonic acid (such asp-methylbenzene sulfonic acid), naphthalene sulfonic acid and oxalicacid or their mixture.

In certain embodiments, the invention relates to any one of theaforementioned methods, wherein the aldehyde-phenol molar ratio is0.8:1-1.2:1, or 0.8:1-1:1.

In certain embodiments, the invention relates to any one of theaforementioned methods, wherein the phenol and aldehyde arereflux-reacted for 1-3 hours at 80-120° C. in the presence of acidiccatalyst, then the reflux condition is changed to distillationcondition, and the reactants react for 0.5-2 hours at 130-200° C., thenneutralizer is added to neutralize the catalyst, and finally distillunder 2-3 kPa of negative pressure to obtain alkyl phenolic resin.

In certain embodiments, the invention relates to the use of any one ofthe aforementioned alkyl phenolic resins in adhesive, dispersant,elastomer, coating, painting, thermoplastic elastomer, ink component andlubricant, or the usage as rubber tackifier.

In certain embodiments, the invention relates to a rubber compound,which contains natural rubber, synthetic rubber or their mixture, andany one of the aforementioned alkyl phenolic resins.

EXEMPLIFICATION

The invention now being generally described, it will be more readilyunderstood by reference to the following examples which are includedmerely for purposes of illustration of certain aspects and embodimentsof the present invention, and are not intended to limit the invention.

General Materials and Methods

The C8 alkene used in Examples 1 to 5 was obtained through non-selectivepolymerization of C4 alkene. The non-selective polymerization processused as raw material the mixture of 54.8% (w/w) of 1-butylene, 16.5%(w/w) of 2-butylene, 1.5% (w/w) of isobutylene, 23% (w/w) of butane, and4.2% (w/w) of other hydrocarbons. The polymerization was carried out at180-220° C. in the presence of solid phosphoric acid catalyst (i.e.,phosphoric acid loaded onto silicon dioxide). Then, the mixture of thereaction products was rectified to obtain C8 alkene, the main componentsof which included:

Molecular structure % w/w 2,2-dimethyl-3-hexene 3.603,4,4-trimethyl-1-pentene 2.17 trans-5,5-dimethyl-1-hexene 0.932,4,4-trimethyl-2-pentene 1.24 3-isopropyl-1-pentene 9.80trans-2,4-dimethyl-3-hexene 4.19 4,4-dimethyl-2-hexene 10.742-isopropyl-1-pentene 2.02 2,3,4-trimethyl-1-pentene 2.242,3-dimethyl-1-hexene 1.21 3,4,4-trimethyl-2-pentene 7.602,3-dimethyl-3-hexene 12.52 3-isopropyl-2-pentene 6.083,5-dimethyl-2-hexene 0.73 2-ethyl-3-hexene 6.472,3,4-trimethyl-2-pentene 14.32 2-ethyl-1-hexene 0.493-methyl-3-heptylene 0.37 cis-2,3-dimethyl-3-hexene 3.073-ethyl-2-hexene 2.41 trans-2,3-dimethyl-3-hexene 6.84

DIB was supplied by Chemiway Maruzen Petrochemical (Japan), with purityover 97%.

Nonylphenol was purchased from Beijing Chemical Reagent Corp., withpurity over 99%.

The apparatus used to measure softening point was a Mettler Toledo FP90calorific value analysis system +FP83HT (Mettler Toledo).

PTOP-formaldehyde resin (“203 resin”) was supplied by Wuhan Jinghe. Itssoftening point was 99° C., and it had 3.87% w/w free phenol.

PTOP was purchased from Shandong Luhua Haoyuan Chemical Co., Ltd., withpurity over 95% w/w.

The molecular weights of polymers were measured by a Waters 2695 GPCsystem (Waters, US) with a Waters 2414 detector (solvent: THF; flowrate: 1.0 mL/min; column temperature: 35° C.; GPC column:HR3+HR1+HR0.5).

The content of free phenol was measured by a Waters 2695 HPLC 2996PPA(solvent: THF+water+methanol; flow rate: 1.0 mL/min; temperature: 30°C.; column: Waters Sunfire C18, 250 mm×4.6 mm).

All molecular weights, including number average and weight averagemolecular weights, unless otherwise indicated, are “g/mol.”

EXAMPLE 1

In a 500-mL four-neck round-bottom flask mounted with mechanicalstirrer, thermometer, reflux condenser and dropping funnel, add 94 g ofphenol and 4.7 g of ionic exchange resin (Rohm and Haas, Amberlyst A-15,5% of phenol weight); heat up to 85° C. while stirring; add 112 g ofmixed octylene [mixture of C8 alkene (20% w/w) and DIB (80% w/w)] withdropping funnel; control the dropping speed so it completes in about 2hours, and maintain the reaction temperature at 90° C.; after completionof dropping, keep reacting for 3 hours at 90° C.; GC analysis revealsthat the reaction solution contains alkyl phenol (88.09% w/w), alkene(7.82% w/w) and unreacted phenol. At 160-170° C., distill to obtainunreacted alkene, and separate alkyl phenol 1; in the alkyl phenol 1,the content of octylphenol is 84.6% w/w, in which the content of PTOP is68% w/w; furthermore, the content of dioctyl phenol is 12.2% w/w, inaddition to small amounts of dodecylphenol, phenol, etc.

EXAMPLE 2

In a 500-mL four-neck round-bottom flask mounted with mechanicalstirrer, thermometer, reflux condenser and dropping funnel, add 94 g ofphenol and 4.7 g of ionic exchange resin (Rohm and Haas, Amberlyst A-15,5% of phenol weight); heat up to 85° C. while stirring; add 117.6 g ofmixed octylene [mixture of C8 alkene (40% w/w) and DIB (60% w/w)] withdropping funnel; control the dropping speed so it completes in about 2hours, and maintain the reaction temperature at 90° C.; after completionof dropping, keep reacting for 3 hours at 90° C.; GC analysis revealsthat the reaction solution contains alkyl phenol (86.15% w/w), alkene(9.33% w/w) and unreacted phenol. At 160-170° C., distill to obtainunreacted alkene, and separate alkyl phenol 2; in the alkyl phenol 2,the content of octylphenol is 77.4% w/w, in which the content of PTOP is54.5% w/w; furthermore, the content of dioctyl phenol is 17.8% w/w, inaddition to small amounts of dodecylphenol, phenol, etc.

EXAMPLE 3

In a 500-mL four-neck round-bottom flask mounted with mechanicalstirrer, thermometer, reflux condenser and dropping funnel, add 94 g ofphenol and 4.7 g of ionic exchange resin (Rohm and Haas, Amberlyst A-15,5% of phenol weight); heat up to 85° C. while stirring; add 123g ofmixed octylene [mixture of C8 alkene (60% w/w) and DIB (40% w/w)] withdropping funnel; control the dropping speed so it completes in about 1hours, and maintain the reaction temperature at 90° C.; after completionof dropping, keep reacting for 3 hours at 90° C.; GC analysis revealsthat the reaction solution contains alkyl phenol (86.2% w/w), alkene(10.25% w/w) and unreacted phenol. At 160-170° C., distill to obtainunreacted alkene, and separate alkyl phenol 3; in the alkyl phenol 3,the content of octylphenol is 66.6% w/w, in which the content of PTOP is33.4% w/w; furthermore, the content of dioctyl phenol is 26.4% w/w, inaddition to small amounts of dodecylphenol, phenol, etc.

EXAMPLE 4

In a 500-mL four-neck round-bottom flask mounted with mechanicalstirrer, thermometer, reflux condenser and dropping funnel, add 94 g ofphenol and 4.7 g of ionic exchange resin (Rohm and Haas, Amberlyst A-15,5% of phenol weight); heat up to 85° C. while stirring; add 134g ofmixed octylene [mixture of C8 alkene (80% w/w) and DIB (20% w/w)] withdropping funnel; control the dropping speed so it completes in about 1hours, and maintain the reaction temperature at 90° C.; after completionof dropping, keep reacting for 3 hours at 90° C.; GC analysis revealsthat the reaction solution contains alkyl phenol (82.86% w/w), alkene(13.04% w/w) and unreacted phenol. At 160-170° C., distill to obtainunreacted alkene, and separate alkyl phenol 4; in the alkyl phenol 4,the content of octylphenol is 61.2% w/w, in which the content of PTOP is15.0% w/w; furthermore, the content of dioctyl phenol is 31.6% w/w, inaddition to small amounts of dodecylphenol, phenol, etc.

Example 5

In a 500-mL four-neck round-bottom flask mounted with mechanicalstirrer, thermometer, reflux condenser and dropping funnel, add 94 g ofphenol and 4.7 g of ionic exchange resin (Rohm and Haas, Amberlyst A-15,5% of phenol weight); heat up to 85° C. while stirring; add 145 g of C8alkene with dropping funnel; control the dropping speed so it completesin about 1 hour, and maintain the reaction temperature at 90° C.; aftercompletion of dropping, keep reacting for 3 hours at 90° C.; GC analysisreveals that the reaction solution contains alkyl phenol (80.57% w/w),alkene (16.23% w/w) and unreacted phenol. At 160-170° C., distill toobtain unreacted alkene, and separate alkyl phenol 5; in the alkylphenol 5, the content of octylphenol is 55.0% w/w, in which the contentof PTOP is 1.51% w/w; furthermore, the content of dioctyl phenol is36.3% w/w, in addition to small amounts of dodecylphenol, phenol, etc.

EXAMPLE 6

In a 500-mL four-neck round-bottom flask mounted with mechanicalstirrer, thermometer, reflux condenser and dropping funnel, add 103 g(0.5 mole) of alkyl phenol 1 obtained from Example 1 and 0.15 g oflinear alkyl benzene sulfonic acid (catalyst, Nanjing Jiahe HouseholdChemical Co., Ltd., with content of C9-C14 alkyl benzene sulfonic acidno less than 97% w/w); heat up the mixture to 100° C. When thetemperature reaches 95° C., start to drop 33.6 g (0.415 mole) of aqueousformaldehyde (37% w/w) for 30 minutes, upon completion of dropping,reflux-react for 120 minutes. Then change the condenser from refluxcondition to distillation condition, and heat up the reactants to130-135° C.; maintain this temperature and react for 1 hour whilestirring, then heat up to 180° C. Then add 0.12 g of1,8-diazabicyclo(5,4,0)undec-7-ene (DBU) to neutralize the catalyst;after reacting for 15 minutes while stirring, slowly turn on the vacuumto reach maximum vacuum (2.5 kPa) and maintain for 30 minutes to obtainalkyl phenolic resin 1. Pour out the resultant alkyl phenolic resin,cool and weigh; the yield is 95.3%. The softening point of this resinmeasured according to ASTM D3461-97 (2007) is 100.5° C. The content offree alkyl phenol monomer in the resin measured by HPLC is 1.01% w/w.The number-average molecular weight measured by GPC is 950, and theweight-average molecular weight is 1411.

EXAMPLE 7

In a 500-mL four-neck round-bottom flask mounted with mechanicalstirrer, thermometer, reflux condenser and dropping funnel, add 103 g(0.5 mole) of alkyl phenol 2 obtained from Example 2 and 0.15 g oflinear alkyl benzene sulfonic acid (catalyst, Nanjing Jiahe HouseholdChemical Co., Ltd., with content of C9-C14 alkyl benzene sulfonic acidno less than 97% w/w); heat up the mixture to 100° C. When thetemperature reaches 95° C., start to drop 33.6 g (0.415 mole) of aqueousformaldehyde (37% w/w) for 30 minutes, upon completion of dropping,reflux-react for 120 minutes. Then change the condenser from refluxcondition to distillation condition, and heat up the reactants to130-135° C.; maintain this temperature and react for 1 hour whilestirring, then heat up to 180° C. Then add 0.12 g of triethanolamine toneutralize the catalyst; after reacting for 15 minutes while stirring,slowly turn on the vacuum to reach maximum vacuum (2.5 kPa) and maintainfor 30 minutes to obtain alkyl phenolic resin 2. Pour out the resultantalkyl phenolic resin, cool and weigh; the yield is 94.8%. The softeningpoint of this resin measured according to ASTM D3461-97 (2007) is 93° C.The content of free alkyl phenol monomer in the resin measured by HPLCis 1.69% w/w. The number-average molecular weight measured by GPC is928, and the weight-average molecular weight is 1519.

EXAMPLE 8

In a 500-mL four-neck round-bottom flask mounted with mechanicalstirrer, thermometer, reflux condenser and dropping funnel, add 103 g(0.5 mole) of alkyl phenol 3 obtained from Example 3 and 0.15 g oflinear alkyl benzene sulfonic acid (catalyst, Nanjing Jiahe HouseholdChemical Co., Ltd., with content of C9-C14 alkyl benzene sulfonic acidno less than 97% w/w); heat up the mixture to 100° C. When thetemperature reaches 95° C., start to drop 33.6 g (0.415 mole) of aqueousformaldehyde (37% w/w) for 30 minutes, upon completion of dropping,reflux-react for 120 minutes. Then change the condenser from refluxcondition to distillation condition, and heat up the reactants to130-135° C.; maintain this temperature and react for 1 hour whilestirring, then heat up to 180° C. Then add 0.12 g of triethanolamine toneutralize the catalyst; after reacting for 15 minutes while stirring,slowly turn on the vacuum to reach maximum vacuum (2.5 kPa) and maintainfor 30 minutes to obtain alkyl phenolic resin 3. Pour out the resultantalkyl phenolic resin, cool and weigh; the yield is 95.2%. The softeningpoint of this resin measured according to ASTM D3461-97 (2007) is 96.3°C. The content of free alkyl phenol monomer in the resin measured byHPLC is 0.66% w/w. The number-average molecular weight measured by GPCis 1011, and the weight-average molecular weight is 1657.

EXAMPLE 9

In a 500-mL four-neck round-bottom flask mounted with mechanicalstirrer, thermometer, reflux condenser and dropping funnel, add 103 g(0.5 mole) of alkyl phenol 4 obtained from Example 4 and 0.15 g oflinear alkyl benzene sulfonic acid (catalyst, Nanjing Jiahe HouseholdChemical Co., Ltd., with content of C9-C14 alkyl benzene sulfonic acidno less than 97% w/w); heat up the mixture to 100° C. When thetemperature reaches 95° C., start to drop 33.6 g (0.415 mole) of aqueousformaldehyde (37% w/w) for 30 minutes, upon completion of dropping,reflux-react for 120 minutes. Then change the condenser from refluxcondition to distillation condition, and heat up the reactants to130-135° C.; maintain this temperature and react for 1 hour whilestirring, then heat up to 180° C. Then add 0.12g of triethanolamine toneutralize the catalyst; after reacting for 15 minutes while stirring,slowly turn on the vacuum to reach maximum vacuum (2.5 kPa) and maintainfor 30 minutes to obtain alkyl phenolic resin 4. Pour out the resultantalkyl phenolic resin, cool and weigh; the yield is 96%. The softeningpoint of this resin measured according to ASTM D3461-97 (2007) is 92.5°C. The content of free alkyl phenol monomer in the resin measured byHPLC is 0.34% w/w. The number-average molecular weight measured by GPCis 1075, and the weight-average molecular weight is 1812.

EXAMPLE 10

In a 500-mL four-neck round-bottom flask mounted with mechanicalstirrer, thermometer, reflux condenser and dropping funnel, add 103 g(0.5 mole) of alkyl phenol 5 obtained from Example 5 and 0.15 g oflinear alkyl benzene sulfonic acid (catalyst, Nanjing Jiahe HouseholdChemical Co., Ltd., with content of C9-C14 alkyl benzene sulfonic acidno less than 97% w/w); heat up the mixture to 100° C. When thetemperature reaches 95° C., start to drop 33.6 g (0.415 mole) of aqueousformaldehyde (37% w/w) for 30 minutes, upon completion of dropping,reflux-react for 120 minutes. Then change the condenser from refluxcondition to distillation condition, and heat up the reactants to130-135° C.; maintain this temperature and react for 1 hour whilestirring, then heat up to 180° C. Then add 0.12 g of1,8-diazabicyclo(5,4,0)undec-7-ene (DBU) to neutralize the catalyst;after reacting for 15 minutes while stirring, slowly turn on the vacuumto reach maximum vacuum (2.5 kPa) and maintain for 30 minutes to obtainalkyl phenolic resin 5. Pour out the resultant alkyl phenolic resin,cool and weigh; the yield is 94.7%. The softening point of this resinmeasured according to ASTM D3461-97 (2007) is 96.3° C. The content offree alkyl phenol monomer in the resin measured by HPLC is 0.30% w/w.The number-average molecular weight measured by GPC is 1155, and theweight-average molecular weight is 2208.

Comparative Example 1

In a 500-mL four-neck round-bottom flask mounted with mechanicalstirrer, thermometer, reflux condenser and dropping funnel, add 103 g(0.5 mole) of PTOP and 0.15 g of linear alkyl benzene sulfonic acid(catalyst, Nanjing Jiahe Household Chemical Co., Ltd., with content ofC9-C14 alkyl benzene sulfonic acid no less than 97% w/w); heat up themixture to 100° C. When the temperature reaches 95° C., start to drop32.4 g (0.4 mole) of aqueous formaldehyde (37% w/w) for 30 minutes, uponcompletion of dropping, reflux-react for 120 minutes. Then change thecondenser from reflux condition to distillation condition, and heat upthe reactants to 130-135° C.; maintain this temperature and react for 1hour while stirring, then heat up to 180° C. Then add 0.12 g of1,8-diazabicyclo(5,4,0)undec-7-ene (DBU) to neutralize the catalyst;after reacting for 15 minutes while stirring, slowly turn on the vacuumto reach maximum vacuum (2.5 kPa) and maintain for 30 minutes to obtainalkyl phenolic resin C. Pour out the resultant resin, cool and weigh;the yield is 96.8%. The softening point of this resin measured accordingto ASTM D3461-97 (2007) is 96.0° C. The content of free alkyl phenolmonomer in the resin measured by HPLC is 3.29% w/w. The number-averagemolecular weight measured by GPC is 834, and the weight-averagemolecular weight is 1399.

Comparative Example 2

In a 500-mL four-neck round-bottom flask mounted with mechanicalstirrer, thermometer, reflux condenser and dropping funnel, add 103 g(0.5 mole) of PTOP and 0.15 g of linear alkyl benzene sulfonic acid(catalyst, Nanjing Jiahe Household Chemical Co., Ltd., with content ofC9-C14 alkyl benzene sulfonic acid no less than 97% w/w); heat up themixture to 100° C. When the temperature reaches 95° C., start to drop36.5 g (0.45 mole) of aqueous formaldehyde (37% w/w) for 30 minutes,upon completion of dropping, reflux-react for 120 minutes. Then changethe condenser from reflux condition to distillation condition, and heatup the reactants to 130-135° C.; maintain this temperature and react for1 hour while stirring, then heat up to 180° C. Then add 0.12 g of1,8-diazabicyclo(5,4,0)undec-7-ene (DBU) to neutralize the catalyst;after reacting for 15 minutes while stirring, slowly turn on the vacuumto reach maximum vacuum (2.5 kPa) and maintain for 30 minutes. Pour outthe resultant resin, cool and weigh; the yield is 97.7%. The softeningpoint of this resin measured according to ASTM D3461-97 (2007) is 131.6°C. The content of free alkyl phenol monomer in the resin measured byHPLC is 0.46% w/w. The number-average molecular weight measured by GPCis 1774, and the weight-average molecular weight is 4488.

In Comparative Example 2, the content of free alkyl phenol monomer inthe resin is reduced by increasing the use level of formaldehyde,however the softening point of the resultant resin is as high as 131.6°C., which exceeds the range of normal octyl phenolic tackifying resin,and is detrimental to the mixing of the resin with rubber.

EXAMPLE 11

In a 500-mL four-neck round-bottom flask mounted with mechanicalstirrer, thermometer, reflux condenser and dropping funnel, add 20.6 g(0.1 mole) of PTOP, 88 g (0.4 mole) of nonylphenol and 0.15 g of linearalkyl benzene sulfonic acid (catalyst, Nanjing Jiahe Household ChemicalCo., Ltd., with content of C9-C14 alkyl benzene sulfonic acid no lessthan 97% w/w); heat up the mixture to 100° C. When the temperaturereaches 95° C., start to drop 36 g (0.444 mole) of aqueous formaldehyde(37% w/w) for 30 minutes, upon completion of dropping, reflux-react for120 minutes. Then change the condenser from reflux condition todistillation condition, and heat up the reactants to 130-135° C.;maintain this temperature and react for 1 hour while stirring, then heatup to 180° C. Then add 0.12 g of 1,8-diazabicyclo(5,4,0)undec-7-ene(DBU) to neutralize the catalyst; after reacting for 15 minutes whilestirring, slowly turn on the vacuum to reach maximum vacuum (2.5 kPa)and maintain for 30 minutes to obtain alkyl phenolic resin 6. Pour outthe resultant resin, cool and weigh; the yield is 97.6%. The softeningpoint of this resin measured according to ASTM D3461-97 (2007) is 99° C.The content of free alkyl phenol monomer in the resin measured by HPLCis 0.25% w/w. The number-average molecular weight measured by GPC is1691, and the weight-average molecular weight is 2264.

EXAMPLE 12

In a 500-mL four-neck round-bottom flask mounted with mechanicalstirrer, thermometer, reflux condenser and dropping funnel, add 41.2 g(0.2 mole) of PTOP, 66 g (0.3 mole) of nonylphenol and 0.15 g of linearalkyl benzene sulfonic acid (catalyst, Nanjing Jiahe Household ChemicalCo., Ltd., with content of C9-C14 alkyl benzene sulfonic acid no lessthan 97% w/w); heat up the mixture to 100° C. When the temperaturereaches 95° C., start to drop 35 g (0.432 mole) of aqueous formaldehyde(37% w/w) for 30 minutes, upon completion of dropping, reflux-react for120 minutes. Then change the condenser from reflux condition todistillation condition, and heat up the reactants to 130-135° C.;maintain this temperature and react for 1 hour while stirring, then heatup to 180° C. Then add 0.12 g of 1,8-diazabicyclo(5,4,0)undec-7-ene(DBU) to neutralize the catalyst; after reacting for 15 minutes whilestirring, slowly turn on the vacuum to reach maximum vacuum (2.5 kPa)and maintain for 30 minutes to obtain alkyl phenolic resin 7. Pour outthe resultant resin, cool and weigh; the yield is 98.5%. The softeningpoint of this resin measured according to ASTM D3461-97 (2007) is 98.7°C. The content of free alkyl phenol monomer in the resin measured byHPLC is 0.89% w/w. The number-average molecular weight measured by GPCis 1407, and the weight-average molecular weight is 1890.

EXAMPLE 13

In the mixture of natural rubber (Standard Malaysian Rubber, SMR20) andsynthetic butadiene rubber (from Beijing Yanshan Petrochemical Co.,Ltd., BR9000), evaluate the performance of the alkyl phenolic resin fromExamples 6 to 12 of this invention, alkyl phenolic resin fromComparative Example 1 and commercially available 203 resin as tackifyingresin.

The tackiness is measured according to JIS T 9233-1997.

Formulation of rubber compound is shown in Table 1.

TABLE 1 Formulation of rubber compound. Part (by Component weight)Natural rubber 30.0 Butadiene rubber 70.0 Carbon black (N375) 80.0Operating oil 4.0 Stearic acid 2.0 Zinc oxide 3.0 Sulfur 1.0 Sulfenamide(NS) 2.2 Poly(1,2-dihydro-2,2,4-trimethyl-quinoline) (TMQ) 1.5N-(1,2-Dimethylbutyl)-N′-phenyl-p-phenylenediamine (4020) 1.6 Tackifyingresin 4.0

Step 1: Mix butadiene rubber, natural rubber, carbon black, operatingoil, stearic acid and zinc oxide at 150° C. in a banbury mixer to obtainmasterbatch; Step 2: In certain amount of masterbatch, separately addresin of this invention from Examples 6 to 12 (alkyl phenolic resin 1,2, 3, 4, 5, 6 and 7), resin from Comparative Example 1 (alkyl phenolicresin C) and commercially-available 203 resin as tackifying resin, andalso add anti-aging agent TMQ and 4020, and mix at 140° C. in a banburymixer; Step 3: Add sulfur and NS to the rubber stock obtained in Step 2,mix and press in an open mill to obtain rubber sheets 1, 2, 3, 4, 5, 6,7, C and 203. Store these rubber sheets under 23° C. and 50% RH. Measurethe tackiness (in N) after 24, 48 and 72 hours of storage respectively.The tackiness is measured by P-2 tackiness tester (Toyoseiki, Japan).The tackiness results of rubber sheets using different tackifying resinsare listed in Table 2.

After the sheets are left for 24 hours, measure their vulcanizationcharacteristics, the result of which is shown in Table 3. Apparatus usedinclude rotorless curemeter and Mooney viscometer (AFA Technologies,US). Vulcanize the rubber sheet samples on pate vulcanizer. Test thephysical and mechanical properties of the vulcanized rubber before andafter aging. Aging of vulcanized rubber is measured by GBT3512-2001method, in which the vulcanized rubber sheets are placed in hot airaging oven at 100° C. for 24 hours, then removed for physical andmechanical property test, the result of which is shown in Table 4.

TABLE 2 Tackiness results. Tackiness Tackiness Tackiness after 24 after48 after 72 Rubber sheet hours (N) hours (N) hours (N) Rubber sheet 110.74 9.23 8.95 Rubber sheet 2 11.39 12.68 9.33 Rubber sheet 3 11.4510.70 11.15 Rubber sheet 4 14.45 10.50 12.50 Rubber sheet 5 15.97 11.1010.83 Rubber sheet 6 10.57 8.85 8.65 Rubber sheet 7 10.91 10.50 9.35Rubber sheet C 11.1 10.6 8.3 Rubber sheet 203 11.05 9.95 8.95

TABLE 3 Vulcanization characteristics of rubber sheet. Rubber sheet 4Rubber sheet 203 Mooney viscosity MS(1 + 4)/100° C. 48.96 47.97 MS(1 +8)/100° C. 46.62 45.24 Scorching time (127° C.) Ts2 15:57 16:17 Ts517:44 17:19 Vulcanization characteristics (160 × 30 min ° C.) T10 04:2804:16 T50 06:06 06:00 T90 08:51 10:27 ML  3.34  3.38 MH 22.66 21.34

TABLE 4 Physical and mechanical properties of vulcanized rubber sheet.Rubber sheet 4 Rubber sheet 203 Physical and mechanical propertiesbefore aging 50% modulus, MPa 2.61 2.38 100% modulus, MPa 4.88 4.44Tensile strength, MPa 20.96 21.17 Elongation at break, % 281 292Physical and mechanical properties after aging, 100° C., 24 h 50%modulus, MPa 3.45 3.04 100% modulus, MPa 6.68 5.86 Tensile strength, MPa20.17 19.92 Elongation at break, % 225 244

The aforementioned data shows that, the alkyl phenolic resin of thisinvention has low content of residual phenol, while maintainingexcellent tackiness, as well as processing performance and mechanicalproperties substantially similar to commercial products.

REFERENCES

All publications and patents mentioned herein, including those itemslisted below, are hereby incorporated by reference in their entirety asif each individual publication or patent was specifically andindividually indicated to be incorporated by reference. In case ofconflict, the present application, including any definitions herein,will control.

EQUIVALENTS

Although the embodiments of this invention have been described as abovefor the purpose of elucidation, without departing from the scope of thisinvention, it will be apparent to those skilled in the art that variousmodifications and variation can be made to this invention.

1. A method, comprising: providing an alkyl phenol mixture comprising analkyl phenol and a second phenol, and reacting the alkyl phenol mixturewith an aldehyde to form an alkyl phenolic resin, wherein the secondphenol is different from the alkyl phenol; and the second phenol ispresent in a concentration up to 10% by weight of the alkyl phenolmixture.
 2. The method of claim 1, wherein the second phenol is phenol.3. The method of claim 1, wherein the second phenol is selected from thegroup consisting of phenol, m-dihydroxy-benzene, and xylenol.
 4. Themethod of claim 1, wherein the second phenol is present in aconcentration from about 3.2% to about 10% by weight of the alkyl phenolmixture.
 5. The method of claim 1, wherein the aldehyde is selected fromRCHO, wherein R is C1-C8 alkyl.
 6. The method of claim 1, wherein thealkyl group of the alkyl phenol has 6-12 carbon atoms.
 7. The method ofclaim 1, wherein the content of 4-(1,1,3,3- tetramethylbutyl) phenol inthe alkyl phenol is from about 0% to about 85% w/w.
 8. The method ofclaim 1, wherein the alkyl phenol mixture comprises a para-alkylphenol.9. The method of claim 1, wherein the alkyl phenol mixture comprisespara-tert-octyl phenol.
 10. An alkyl phenolic resin prepared by themethod of claim
 1. 11. A composition comprising a polycondensationproduct of (i) an alkyl phenol mixture comprising an alkyl phenol and asecond phenol with (ii) an aldehyde; wherein the second phenol isdifferent from the alkyl phenol; and the second phenol is present in aconcentration up to about 10% by weight of the alkyl phenol mixture. 12.The composition of claim 11, the second phenol is phenol.
 13. Thecomposition of claim 11, wherein the second phenol is selected from thegroup consisting of phenol, m-dihydroxy-benzene, and xylenol.
 14. Thecomposition of claim 11, wherein the second phenol is present in aconcentration from about 3.2% to about 10% by weight of the alkyl phenolmixture.
 15. The composition of claim 11, wherein the aldehyde isselected from RCHO, wherein R is Cl-C8 alkyl.
 16. The composition ofclaim 11, wherein the composition comprises residual phenol in an amountof from about 0% to about 2% by weight.
 17. The composition of claim 11,wherein the composition has a softening point of about 85° C. to about105° C.
 18. The composition of claim 11, wherein the composition has atackiness from about 8 N to about 25 N.
 19. The composition of claim 11,wherein the alkyl group of the alkyl phenol has 6-12 carbon atoms. 20.The composition of claim 11, wherein the content of 4-(1,1,3,3-tetramethylbutyl) phenol in the alkyl phenol is from about 0% to about85% w/w.
 21. A rubber article, wherein the rubber article comprises (i)a rubber component, and (ii) the composition of claim
 11. 22. A rubbercomposition comprising the composition of claim 11, and a naturalrubber, a synthetic rubber, or a mixture thereof.
 23. A tire comprisingthe composition of claim
 11. 24. A tire comprising the rubbercomposition of claim 22.